王楚乔;王光阳;宋远明;

• 1:烟台大学环境与材料工程学院

摘要(Abstract)：

将碳酸钙、硝酸钙和氯化钠分别掺入到普通硅酸盐水泥中，采用XRD分析、热分析、净浆线性膨胀率及胶砂抗压强度测试，研究了它们对水泥水化及宏观性能的影响。结果显示，这3种组分所引入的阴离子会参与水泥水化，生成相应的AFm相，且能够增加钙矾石含量，从而提升净浆线性膨胀率，并在一定范围提升胶砂抗压强度。研究表明，CO_3^(2-)、NO_3(2-)、NO_3^-或Cl-或Cl^-都能够提高钙矾石稳定性，从而改善水泥性能，对钙矾石稳定性的提升能力顺序为Cl-都能够提高钙矾石稳定性，从而改善水泥性能，对钙矾石稳定性的提升能力顺序为Cl^->NO_3->NO_3^->CO_3->CO_3^(2-),但Cl(2-),但Cl^-仅起早强作用，会抑制7 d之后龄期强度发展。

关键词(KeyWords)： 普通硅酸盐水泥;钙矾石;稳定性;AFm相

Abstract:

Keywords:

基金项目(Foundation): 国家自然科学基金资助项目(51272222)

作者(Authors): 王楚乔;王光阳;宋远明;

DOI: 10.13951/j.cnki.37-1213/n.210101

参考文献(References)：

• [1] 钱觉时，余金城，孙化强，等.钙矾石的形成与作用[J].硅酸盐学报，2017,45(11):1569-1581. [2] KAKALI G,TSIVILIS S,AGGELI E,et al.Hydration products of C3A,C3S and Portland cement in the presence of CaCO3[J].Cement and Concrete Research,2000,30(7):1073-1077. [3] PELLETIER-CHAIGNAT L,WINNEFELD F,LOTHENBACH B,et al.Beneficial use of limestone filler with calcium sulphoaluminate cement[J].Construction and Building Materials,2012,26(1):619-627. [4] 刘焕芹，徐志峰，李维滨，等.石灰石粉对硅酸盐水泥水化的影响[J].材料科学与工程学报，2015,33(2):185-188. [5] ZHOU M K,PENG S M,XU J,et al.Effect of stone powder on stone chippings concrete[J].Journal of Wuhan University of Technolugy(Materials Sience,1996,11(4):29-34. [6] SCH?LER A,LOTHENBACH B,WINNEFELD F,et al.Hydration of quaternary Portland cement blends containing blast-furnace slag,siliceous fly ash and limestone powder[J].Cement and Concrete Composites,2015,55:374-382. [7] 郝璟珂，宋远明，王志娟，等.AFm阴离子类型对硫铝酸盐水泥水化产物钙矾石稳定性的影响[J].硅酸盐学报，2019,47(11):1554-1558. [8] MAGDALENA B.The influence of inorganic chemical accelerators and corrosion inhibitors on the mineralogy of hydrated Portland cement systems[D].Aberdeen:University of Aberdeen,2010. [9] FALZONE G,BALONIS M,SANT G.X-AFm stabilization as a mechanism of bypassing conversion phenomena in calcium aluminate cements[J].Cement and Concrete Research,2015,72:54-68. [10] SIDERIS K K,SAVVA A E.Durability of mixtures containing calcium nitrite based corrosion inhibitor[J].Cement and Concrete Composites,2005,27(2):277-287. [11] MURALIDHARAN S,SARASWATHY V,MERLIN NIMA S P,et al.Evaluation of a composite corrosion inhibiting admixtures and its performance in Portland pozzolana cement[J].Materials Chemistry and Physics,2004,86(2-3):298-306. [12] RIVARD P,BéRUBé M A,BALLIVY G,et al.Effect of drying-rewetting on the alkali concentration of the concrete pore solution[J].Cement and Concrete Research,2003,33(6):927-929. [13] 中华人民共和国建设部.混凝土拌合用水标准：JGJ 63—2006[S].北京：中国建筑工业出版社，2006. [14] 国家质量技术监督局.水泥胶砂强度检验方法(IOS法):GB/T 17671—1999[S].北京：中国建筑工业出版社，1999. [15] 中华人民共和国工业和信息化部.膨胀水泥膨胀率试验方法：JC/T 313—2015[S].北京：中国建筑工业出版社，2015. [16] 姚燕，王宏霞，刁桂芝，等.硝酸钙对铝酸盐水泥强度及水化性能的影响[J].硅酸盐学报，2019,47(2):207-213.